GB /T 3098.25 - 2020 Mechanical properties of fasteners-Guidance for the selection of stainless steels and nickel alloys for fasteners

表1 奥氏体不锈钢化学成分（GB/T 3098.6、GB/T3098.15、GB/T 3098.16、GB/T3098.21）

ISO代号	化学成分（质量分数）^a / %												对应的紧固件组别^b
ISO代号	C	Si	Mn	P	S	Cr	Mo	Ni	Cu	N	Nb	Ti	对应的紧固件组别^b
奥氏体不锈钢
4305-303-00-I	0.120	1.00	2.00	0.060	≥0.15	17.0~19.0	/	8.0~10.0	1.0	0.10	/	/	A1
4301-304-00-I	0.070	1.00	2.00	0.045	0.030	17.5~19.5	/	8.0~10.5	/	0.10	/	/	A2
4307-304-03-I	0.030	1.00	2.00	0.045	0.030	17.5~19.5	/	8.0~10.5	/	0.10	/	/	A2L
4311-304-53-I	0.030	1.00	2.00	0.045	0.030	17.5~19.5	/	8.0~11.0	/	0.12~0.22	/	/	A2L
4567-304-98-X	0.080	1.00	2.00	0.045	0.030	17.0~19.0	/	8.0~10.5	1.0~3.0	/	/	/	A2
4567-304-30-I	0.040	1.00	2.00	0.045	0.030	17.0~19.0	/	8.0~10.5	3.0~4.0	0.10	/	/	A3
4541-321-00-I	0.080	1.00	2.00	0.045	0.030	17.0~19.0	/	9.0~12.0	/	/	/	5×C~0.70	A3
4550-347-00-I	0.080	1.00	2.00	0.045	0.030	17.0~19.0	/	9.0~12.0	/	/	10×C~1.00	/	A3
4401-316-00-I	0.080	1.00	2.00	0.045	0.030	16.0~18.0	2.00~3.00	10.0~13.0	/	0.10	/	/	A4
4404-316-03-I	0.030	1.00	2.00	0.045	0.030	16.5~18.5	2.00~3.00	10.0~13.0	/	0.10	/	/	A4L
4406-316-53-I	0.030	1.00	2.00	0.045	0.030	16.5~18.5	2.00~3.00	10.0~12.5	/	0.12~0.22	/	/	A4L
4578-316-76-E	0.040	1.00	2.00	0.045	0.015	16.5~17.5	2.00~2.50	10.0~11.0	3.0~3.5	0.10	/	/	A4
4571-316-35-I	0.080	1.00	2.00	0.045	0.030	16.5~18.5	2.00~2.50	10.5~13.5	/	/	/	5×C~0.70	A5
4529-089-26-I	0.020	0.75	2.00	0.035	0.015	19.0~21.0	6.0~7.0	24.0~26.0	0.5~1.5	0.15~0.25	/	/	A8
4547-312-54-I	0.020	0.70	1.00	0.035	0.015	19.5~20.5	6.0~7.0	17.5~18.5	0.50~1.00	0.18~0.25	/	/	A8
4478-083-67-U	0.030	1.00	2.00	0.040	0.030	20.0~22.0	6.0~7.0	23.5~25.5	0.75	0.18~0.25	/	/	A8
注：表中所列成分除标明范围或最小值外，其余均为最大值。
a 未经买方同意，不宜将未规定的元素加入钢材中，除非为了完成冶炼。应采取一切合理的预防措施，以防止从制造中使用的废料或其他材料中添加影响淬透性、机械性能和适用性的元素。 b 钢的组别与GB/T 3098.6和GB/T 3098.15规定的成分范围最接近，但是，本表中包含的不一定完全符合。

表2 马氏体、铁素体和双相钢化学成分（GB/T 3098.6、GB/T 3098.15、GB/T 3098.16、GB/T 3098.21)

ISO代号	化学成分（质量分数）^a / %												对应的紧固件组别^b
ISO代号	C	Si	Mn	P	S	Cr	Mo	Ni	Cu	N	Nb	Ti	对应的紧固件组别^b
马氏体不锈钢
4006-410-00-I	0.08~0.15	1.00	1.5	0.040	0.030	11.5~13.5	/	0.75	/	/	/	/	C1
4021-420-00-I	0.16~0.25	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	C1
4028-420-00-I	0.26~0.35	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	C1
4057-431-00-X	0.12~0.22	1.00	1.50	0.040	0.030	15.0~17.0	/	1.50~2.50	/	/	/	/	C3
4005-416-00-I	0.08~0.15	1.00	1.50	0.040	≥0.15	12.0~14.0	0.60	/	/	/	/	/	C4
铁素体不锈钢
4016-430-00-I	0.08	1.00	1.00	0.040	0.030	16.0~18.0	/	/	/	/	/	/	F1
双相不锈钢
4482-320-01-X	0.030	1.00	4.0~6.0	0.035	0.030	19.5~21.5	0.10~0.60	1.50~3.50	1.0	0.05~0.20	/	/	D2^d
4362-323-04-I	0.030	1.00	2.00	0.035	0.015	22.0~24.5	0.10~0.60	3.5~5.5	0.10~0.60	0.05~0.20	/	/	D2^d
4062-322-02-U	0.030	1.00	2.00	0.040	0.010	21.5~24.0	0.45	1.00~2.90	/	0.16~0.28	/	/	D4
4162-321-01-E	0.040	1.00	4.0~6.0	0.040	0.015	21.0~22.0	0.10~0.80	1.35~1.90	0.10~0.80	0.20~0.25	/	/	D4
4662-824-41-X	0.030	0.70	2.50~4.0	0.035	0.005	23.0~25.0	1.00~2.00	3.0~4.5	0.10~0.80	0.20~0.30	/	/	D4
4462-318-03-I	0.030	1.00	2.00	0.035	0.015	21.0~23.0	2.5~3.5	4.5~6.5	/	0.10~0.22	/	/	D6
4481-312-60-J	0.030	1.00	1.50	0.040	0.030	24.0~26.0	2.5~3.5	5.5~7.5	/	0.08~0.30	/	/	D6
4410-327-50-E	0.030	1.00	2.00	0.035	0.015	24.0~26.0	3.0~4.5	6.0~8.0	/	0.24~0.35	/	/	D8
4501-327-60-I ^c	0.030	1.00	1.00	0.030	0.010	24.0~26.0	3.0~4.0	6.0~8.0	0.5~1.0	0.20~0.30	/	/	D8
4507-325-20-I	0.030	0.70	2.00	0.035	0.015	24.0~26.0	3.0~4.0	6.0~8.0	1.0~2.5	0.20~0.30	/	/	D8
注：表中所列成分除标明范围或最小值外，其余均为最大值。
a 未经买方同意，不宜将未规定的元素加入钢材中，除非为了完成冶炼。应采取一切合理的预防措施，以防止从制造中使用的废料或其他材料中添加影响淬透性、机械性能和适用性的元素。 b 钢的组别与GB/T 3098.6和GB/T 3098.15规定的成分范围最接近，但是，本表中包含的不一定完全符合。 c 钨的含量应为0.5%~1.0%。 d 当wCr＋3.3wMo＋16wN＞24和符合GB/T 3098不锈钢系列标准时，可被认同为D4。

表3 高温不锈钢和镍合金化学成分（GB/T 3098.6、GB/T 3098.15、GB/T 3098.16、GB/T 3098.21）

ISO代号	化学成分（质量分数）^a / %												对应的紧固件组别^b
ISO代号	C	Si	Mn	P	S	Cr	Mo	Ni	Cu	N	Nb	Ti	对应的紧固件组别^b
马氏体不锈钢
4021-420-00-I	0.16~0.25	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	CH0
4028-420-00-I	0.26~0.35	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	CH1
4057-431-00-X	0.12~0.22	1.00	1.50	0.040	0.030	15.0~17.0	/	1.50~2.5	/	/	/	/	CH2
4923-422-77-E^c	0.18~0.24	0.50	0.40~0.90	0.025	0.015	11.0~12.5	0.8~1.2	0.30~0.80	/	/	/	/	V或VH
1.4913^d	0.17~0.23	0.50	0.40~0.90	0.025	0.015	10.0~11.5	0.50~0.80	0.20~0.60	/	0.05~0.10	0.25~0.55	/	VW
奥氏体沉淀硬化不锈钢和镍合金
4980-662-86-X^c	0.08	1.00	2.00	0.040	0.030	13.5~16.0	1.0~1.5	24.0~27.0	/	/	/	1.90~2.35	SD
2.4952^f	0.04~0.10	1.00	1.00	0.020	0.015	18.0~21.0	/	≥65	0.20	/	/	1.80~2.70	SB
2.4668^g	0.02~0.08	0.035	0.035	0.015	0.015	17.0~21.0	2.80~3.30	50.00~55.00	0.30	/	/	0.60~1.20	718
注：表中所列成分除标明范围或最小值外，其余均为最大值。
a 未经买方同意，不宜将未规定的元素加入钢材中，除非为了完成冶炼。应采取一切合理的预防措施，以防止从制造中使用的废料或其他材料中添加影响淬透性、机械性能和适用性的元素。 b 钢的组别与GB/T 3098.6和GB/T 3098.15规定的成分范围最接近，但是，本表中包含的不一定完全符合。 c 此外，钒的含量应为0.25%~0.35%。 d 化学成分与EN 10269一致；此外，铝含量应≤0.020%，钒含量应为0.10%~0.30%，硼含量≤0.0015%。 e 此外，铝含量应≤0.35%，钒含量应为0.10%~0.50%，硼含量0.001%~0.010%。 f 化学成分与EN 10269一致；此外铝含量应为1.00%~1.80%，钴含量应≤1.00%，铁含量≤1.50%，硼含量≤0.008%。 g 化学成分与EN 10269一致；此外铝含量应为0.30%~0.70%，钴含量应≤1.00%，硼含量0.002%~0.006%，铌含量应为4.7%~5.50%（其余为铁）。

表A.1 冷镦紧固件用主要不锈钢常用牌号一奥氏体等级

表A.1 冷镦紧固件用主要不锈钢常用牌号一奥氏体等级^a

类别	组别^h	ISO 15510代号	欧洲材料		ASTM标准中代号	美国常用牌号	GB/T 3098 系列标准中位置	GB/T 20878中代号	相关标准
类别	组别^h	ISO 15510代号	代号	牌号	ASTM标准中代号	美国常用牌号	GB/T 3098 系列标准中位置	GB/T 20878中代号	相关标准
加硫奥氏体	A1	4305-303-00-I	1.4305	X8CrNiS18-9	S30300	303	第 5 章，表1	S30317	ASTM A959，EN 10088-3
加硫奥氏体	A1	4570-303-31-I	1.4570	X6CrNiCuS18-9-2	S30331	303Cu	GB/T 3098.6 GB/T 3098.15	-	EN 10088-3
一般用途奥氏体一般用途奥氏体	A2L	4307-304-03-I	1.4307	X2CrNi18-9	S30403	304L	第 5 章，表1	S30403	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
	A2L	4306-304-03-I	1.4306	XZCrNi19-11	S30403	304L	GB/T 3098.6 GB/T 3098.15	S30403	ASTM A959，EN 10088-3，EN 10263-5
	A2L	4311-304-53-I	1.4311	X2CrNiN18-9	S30453	304LN	第5章，表1	S30453	ASTM A959，EN 10088-3
	A2	4311-304-00-I	1.4301	X5CrNi18-10	S30400	304	第5章，表1	S30408	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
	A2	4567-304-30-I	1.4567^c	X3CrNiCu18-9-4	S30430	304Cu	第5章，表1	S30488	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
	A2	4560-304-75-E	1.4560	X3CrNiCu19-9-2	-	304Cu	GB/T 3098.6 GB/T 3098.15		EN 10088-3，EN 10263-5
	A2	4303-305-00-I	1.4303	X4CrNi18-12	S30500	305	GB/T 3098.6 GB/T 3098.15	S30510	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
	A3	4550-347-00-I	1.4550	X6CrNiNb18-10	S34700	347	第5章，表1	S34778	EN 10088-1
	A3	4541-321-00-I	1.4541	X6CrNiTi18-10	S32100	321	第5章，表1	S32168	ASTM A959，EN 10088-3，EN 10263-5
	^d	4615-201-75-E	1.4615	X3CrMnNiCu15-8-5-3		201Cu			EN 10088-3
	^d	4310-301-00-I	1.4310	Xl0CrNi18-8	S30100	301		S30110	ASTM A959，EN 10088-3，EN 10263-5
含钼奥氏体	A4	4401-316-00-I	1.4401	X5CrNiMo17-12-2	S31600	316	第5章，表1	S31608	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
	A4L	4404-316-03-I	1.4404	X2CrNiMo17-12-2	S31603	316L	第5章，表1	S31603	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
	A4L	4406-316-53-I	1.4406	X2CrNiMoN17-11-2	S31653	316LN	第5章，表1	S31653	ASTM A959，EN 10088-3
	A4L	4432-316-03-I	1.4432	X2CrNiMo17-12-3	S31603	316L	GB/T 3098.6 GB/T 3098.15	S31603	ASTM A959，EN 10088-1，EN 10263-5
	A4L	4435-316-91-I	1.4435	X2CrNiMo18-14-3	S31603	316L	GB/T 3098.6 GB/T 3098.15	S31603	ASTM A959，EN 10088-3
	A4	4436-316-00-I	1.4436	X3CrNiMo17-13-3	331600	316	GB/T 3098.6 GB/T 3098.15	S31608	GB/T 20878，ASTM A959，EN 10088-3，EN 10263-5
	A4	4578-316-76-E	1.4578	X3CrNiCuMo17-11-3-2			第5章，表1		EN 10088-3，EN 10263-5
	A5	4571-316-35-I	1.4571	X6CrNiMoTi17-12-2	S31635	316T1	第5章，表1	S31668	ASTM A959，EN 10088-3，EN 10263-5
高钼超级奥氏体	AS	4478-083-67-U	1.4478	X2NiCrrMoN25-21-7	N08367		第5章，表1		ASTM A959，EN 10088-1
	AS	4529-089-26-I	1.4529	XlNiCrMoCuN25-20-7	N08926	926	第5章，表l		ASTM A959，EN 10088-1
	AS	4547-312-54-I	1.4547	XlCrNiMoCuN20-18-7	S31254	F44	第5章，表1	S31252	ASTM A959，EN 10088-1
特殊用途高合金奥氏体	SD^e.f	4980-662-86-X	1.4980	X6NiCrTiMoVB25-15-2	S66286	A286 合金 660	GB/T 3098.8 GB/T 3098.24 第5章，表3	S51525 GH2132 (GB/T 14992)	ASTM A959，EN 10088-3，EN 10269，DIN 267-13
	S^e		1.4986	X7CrNiMoBNb16-16			GB/T 3098.8		EN 10088-1，EN 10269，DIN 267-13
	^d	4539-089-04-l	1.4539	XlNiCrMoCu25-20-5	N08904	904L		S39042	ASTM A959，EN 10088-3
	^d	4841-314-00-E	1.4841	Xl5CrNiSi25-21	S31400	314			ASTM A959，EN 10088-1
	^d	4828-305-09-l	1.4828	Xl5CrNiSi20-12					ASTM A959，EN 10088-1
	^d	4845-310-08-E	1.4845	X8CrNi25-21	S31008	310S		S31008	ASTM A959，EN 10088-1
高锰超级奥氏体	^d	4020-241-00-X	1.4020	Xl3CrMnNiN18-13-2	S24100	XM28			ASTM A959，EN 10088-3
高锰超级奥氏体	^d	4378-240-00-X	1.4378	X6CrMnNiNl8-13-3	S24000	XM29			ASTM A959，EN 10088-3
高镍超级奥氏体	SB^e^，f		2.4952	NiCr20TiAl	N07080	合金80A	GB/T 3098.24	GH4080A (GB/T 14992)	ASTM B637，EN 10269，DIN 267-13
高镍超级奥氏体	718^f		2.4668	NiCr19NbMo	N07718	合金718	GB/T 3098.24	GH4169 (GB/T 14992)	ASTM B637，EN 10269，DIN 267-13
a 各种标准的组成之间没有确切的对应关系，但多数重叠。 b 组别符合GB/T 3098中不锈钢机械性能系列标准规定。 c 根据EN 10263-5，镍最低含量通常为8% 。 d 特殊等级，在GB/T 3098.6、GB/T 3098.15或GB/T 3098.8 中未规定。 e 代号符合GB/T 3098.8。 f 由GB/T3098.24规定的。

表A.2 冷镦紧固件用主要不锈钢常用牌号一铁素体、马氏体和双相钢等级

表A.2 冷镦紧固件用主要不锈钢常用牌号一铁素体、马氏体和双相钢等级^a

类别	组别^b	ISO 15510代号	欧洲材料		ASTM标准中代号	美国常用牌号	GB/T 3098系列标准中位置	GB/T 20878中代号	相关标准
类别	组别^b	ISO 15510代号	代号	牌号	ASTM标准中代号	美国常用牌号	GB/T 3098系列标准中位置	GB/T 20878中代号	相关标准
一般用途马氏体钢	C1	4006-410-00-I	1.4006	X12Cr13	S41000	410	第5章，表2	S41010	ASTM A959 ，EN 10088-3，EN 10263-5
	C1	4000-410-08-I	1.4000	X6Cr13	S41008	410S	GB/T 3098.6 GB/T 3098.15	S41008	ASTM A959，EN 10088-3
	C1，CH0^c	4021-420-00-I	1.4021	X20Cr13	S42000	420	第5章，表2 GB/T 3098.6 GB/T 3098.15 GB/T 3098.24	S42020	ASTM A959，EN 10088-3
	C1，CH1^c	4028-420-00-I	1.4028	X30Cr13	S42000	420	第5章，表2 GB/T 3098.6 GB/T 3098.15 GB/T 3098.24	S42030	ASTM A959 ，EN 10088-3
	C1	4034-420-00-I	1.4034	X46Cr13	S42000	420	GB/T 3098.6 GB/T 3098.15	S42040	ASTM A959，EN 10088-3
	^d	4003-410-77-I	1.4003	X19CrMoNbVN11-1	S41003			S11213	ASTM A959，EN 10088-1
	VW^c^，e		1.4913	X19CrMoNbVN11-1			GB/T 3098.8 GB/T 3098.24		EN 10088-1，EN 10269，DlN 267-13
	V或VH^c^，e	4923-422-77-E	1.4923	X22CrMoV12-1			第5章，表3 GB/T 3098.8 GB/T 3098.24		EN 10088-1，EN 10269，DIN 267-13
高铬马氏体	C3，CH2^c	4057-431-00-X	1.4057	X17CrNi16-2	S43100	431	第5章，表3 GB/T 3098.24	S43120	ASTM A959，EN 10088-3
	^d	4542-174-00-I	1.4542^f	X5CrNiCuNb16-4	S17400	17-4PH		S51740	ASTM A959，EN 10088-3
	^d	4418-431-77-E	1.4418	X4CrNiMo16-5-1					EN 10088-3
	^d	4122-434-09-I	1.4122	X39CrMo17-1					EN 10088-3
加硫马氏体	C4	4005-416-00-I	1.4005	X12CrS13	S41600	416	第5章，表2	S41617	ASTM A959，EN 10088-3
加硫马氏体	C4	4029-420-20-I	1.4029	X29CrS13	S42020	420F	GB/T 3098.6， GB/T 3098.15	S42037	ASTM A959，EN 10088-3
铁素体	F1	4016-430-00-I	1.4016	X6Cr17	S43000	430	第5章，表2	S11710	ASTM A959，EN 10088-3，EN 10263-5
	F1	4511-430-71-I	1.4511	X3CrNb17			GB/T 3098.6， GB/T 3098.15		EN 10088-3
	F1	4113-434-00-I	1.4113	X6CrMo17-1	S43400	434	GB/T 3098. 6， GB/T 3098.15	S11790	ASTM A959，EN 10088-3，EN 10263-5
	F1	4526-436-00-I	1.4526	X6CrMoNb17-1	S43600	436	GB/T 3098. 6， GB/T 3098.15	S11770	ASTM A959，EN 10088-3
	F1	4509-439-40-X	1.4509	X2CrT iNb18	S43940	441	GB/T 3098.6， GB/T 3098.15	S11873	ASTM A959，EN 10088-3
	F1	4521-444-00-I	1.4521	X2CrMoTi18-2	S44400	444	GB/T 3098.6， GB/T 3098.15	S11972	ASTM A959，EN 10088-2
加硫铁素体	^d	4004-430-20-I	1.4004	X7CrS17	S43020	430F		S11717	ASTM A959，EN 10088-1
加硫铁素体	^d	4019-430-20-I	1.4104	X14CrMoS17	S43020	430F			ASTM A959，EN 10088-3
双相钢	D2^g	4482-320-01-X	1.4482^h	X2CrMnNiMoN21-5-3	S32001	2001	第5章，表2， GB/T 3098.6， GB/T 3098.15		ASTM A959，EN 10088-3
	D2^g	4362-323-04-I	1.4362^h	X2CrNiN23-4	S32304	2304	第5章，表2， GB/T 3098.6， GB/T 3098.15		ASTM A959，EN 10088-3
	D4	4162-321-01-E	1.4162^h	X2CrMnNiN21-5-1	S32101	2101	第5章，表2 GB/T 3098.6， GB/T 3098.15	S23043	ASTM A959，EN 10088-3
双相钢	D4	4062-322-02-U	1.4062^h	X2CrNiN22-2	S32202	2202	第5章，表2， GB/T 3098.6， GB/T 3098.15		ASTM A959，EN 10088-3
	D6	4462-318-03-I	1.4462	X2CrNiMoN22-5-3	S31803 S32205	1803,2205	第5章，表2， GB/T 3098.6， GB/T 3098.15	S22053	ASTM A959，EN 10088-3，EN 10263-5
	D6	4481-312-60-J	1.4481	X2CrNiMoN25-7-3	S31260	SUS329J4Li	第5章，表2， GB/T 3098.6， GB /T 3098.15	S22583	ASTM A959，EN 10088-1
	D8	4410-327-50-E	1.4410	X2CrNiMoN25-7-4	S32750	2507	第5章，表2， GB/ T 3098.6， GB/ T 3098.15	S25073	ASTM A959，EN 10088-3
	D8	4501-327-60-I	1.4501	X2CrNiMoCuWN25-7-4	S32760	-	第5章，表2， GB/T 3098.6， GB/T 3098.15	S27603	ASTM A959，EN 10088-3
	D8	4507-325-20-I	1.4507	X2CrNiMoCuN25-6-3	S32520	-	第5章，表2， GB/T 3098.6， GB/T 3098.15	S25554	ASTM A959，EN 10088-3
a 各种标准的组成之间没有确切的对应关系，但多数重叠。 b 组别符合GB/T 3098中不锈钢机械性能系列标准规定。 C 由GB/T 3098.24规定的代号。 d 特殊等级，在GB/T 3098.6，GB/T 3098.15或 GB/ T 3098.8中未规定。 e代号符合GB/T 3098.8。 f所谓的沉淀硬化等级( PH ) 是低碳、改善韧性和耐腐蚀性的马氏体钢。 g 当ωC_r + 3.3ω Mo + 16ωN > 24.0 和符合GB/T 3098不锈钢系列标准时，可被认同为D4。 h 所谓的“低双相”钢等级，镍和钼含显较低。 j 根据JIS G 4308。